Composition for preparing artificial stone materials

ABSTRACT

A composition for preparing artificial stone materials has the following formulation (mass %): 
     soluble glass: 3-65 
     limestone: 1-75 
     aqueous solution of an acid with pH 1-4: 5-52 
     This composition ensures the production of a wide range of high-strength structural and heat insulating materials.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to building materials on a cement-free base and more particularly to a composition for preparing artificial stone materials.

2. Description of the Related Art

Known in the art is a composition for preparing construction stone materials (SU, A, 808470), having the following formulation (mass %):

boric acid: 10-20

limestone: 70-80

water: up to 100

The material prepared from such a composition has a high ultimate compressive strength, 63.0 MPa, but features an enhanced brittleness, since it has a low ultimate bending strength, 7.0 MPa. For this reason this material has a limited application.

A composition is known for preparing construction artificial stone materials (SU, A, 464560), having the following formulation (mass %):

liquid glass: 15-25

ash: 10-30

aluminium powder: 0.003-0.005

limestone: up to 100

Liquid glass, having a constant sodium silicate component/water ratio, fails to ensure high strength characteristics of the materials prepared from such a composition (ultimate compressive strength, 42.0 MPa; ultimate bending strength, 10.0 MPa; the frost resistance of the material does not exceed 100 cycles). Such a composition is poorly adaptable to the method of semi-dry pressing, since liquid glass, because of its viscosity, is difficult to mix with dry components and is liable to segregation upon prolonged storage.

A composition is known for preparing a heat insulating material (SU, A, 863575), comprising the following components (mass %):

liquid glass: 92-95.5

dry silica: 1.5-2.4

boric acid: 3.0-6.0

The material prepared from this composition is characterized by a low heat conductivity (λ=0.06 W/m·K) due to the average density of up to 200 kg/m³, but it has low ultimate compressive strength, 0.41 MPa, and ultimate bending strength, 0.08 MPa, which limits its application as a building heat insulating material. The coefficient of water resistance is smaller than 0.5, so that the material cannot be used in a medium with an elevated humidity.

Also known is a composition for preparing refractory stone materials (SU, A, 763280), comprising the following components (mass %):

cullet: 20-50

basic blast furnace slag: 50-80

The material prepared from this composition by sintering at a temperature of up to 750° C. with an average density of 1800 kg/cm³ is characterized by the ultimate compressive strength of 21 MPa and ultimate bending strength of 2 MPa, which become appreciably reduced at a temperature above 800° C., so that the application of this material, for instance, as heat-resistant blocks or high-temperature insulation for industrial units and equipment, is limited, insofar as the service temperature of these items exceeds 1000° C.

The main object of the invention is to provide such a composition for preparing artificial stone materials by appropriate qualitative and quantitative selection of the components, which would ensure enhanced compressive and bending strength characteristics of said materials under different service temperature conditions, as well as a low heat conductivity thereof.

SUMMARY OF THE INVENTION

Said object is accomplished by the provision of a composition for preparing artificial stone materials, comprising a silicate component and limestone, which, according to the invention, additionally comprises an aqueous solution of an acid with pH 1-4, and as the silicate component it comprises liquid glass with the following ratio of the components (mass %):

soluble glass: 3-65

limestone: 1-75

aqueous solution of an acid with pH 1-4: 5-52

Such a composition, depending on the ratio of the components, ensures the preparation of a wide range of high-strength construction materials with improved frost-resistance and water-resistance characteristics. The use of soluble glass and such an aqueous acid solution in the composition provides a possibility for preparing materials by using the techniques of semidry pressing, casting, vibrocompacting, and extrusion for shaping thereof. With a decrease of the amount of soluble glass and an increase of the amount of limestone in the composition, the resulting construction material is characterized by the following parameters:

average density, kg/m³ : 1000-2100

ultimate compressive strength, MPa: 5.0-78.0

ultimate bending strength, MPa: 3.0-30.0

frost resistance, cycles: up to 400

An increase of the content of liquid glass and a decrease of the content of limestone in the composition make it possible to prepare a heat insulating material with the following characteristics:

average density, kg/m³ : 100-10000

ultimate compressive strength, MPa: 0.3-20.0

ultimate bending strength, MPa: 0.3-9.0

heat conductivity, W/m·K: 0.035-0.21

It is recommended that for preparing heat insulating and construction materials with high strength characteristics a composition should be used comprising also a silicate component with the content of silicon dioxide exceeding 60 mass %, with the following ratio of the components (mass %):

soluble glass: 3-40

silicate component with the content of silicon dioxide exceeding 60 mass %: 1-70

limestone: 1-70

aqueous acid solution with pH 1-4: 5-52

For construction materials with optimal strength characteristics it is expedient to use a composition having the following formulation (mass %):

soluble glass: 9-15

silicate component with the content of silicon dioxide exceeding 60 mass %: 1-70

limestone: 1-70

aqueous acid solution with pH 2-4: 5-52

For preparing a material with optimal heat insulating properties, high coefficient of water resistance, and strength parameters, it is reasonable to use a composition of the following formulation (mass %):

soluble glass: 20-40

silicate component with the content of silicon dioxide exceeding 60 mass %: 20-40

limestone: 2-10

aqueous acid solution with pH 1-3: 5-52

As said silicate component it is desirable to use cullet or tripoli clays and as said aqueous acid solution, waste water of different acid-manufacturing processes. The introduction of such components into the composition makes the latter appreciably cheaper and makes it possible to utilize industrial wastes, while preserving high strength characteristics of the material prepared from the composition.

Furthermore, the heat-resistant properties of the material become higher, that is, the material retains its working strength on compression at the temperature of 1000° C.

For preparing materials with good heat-resistant properties at a temperature above 1000° C., it is desirable to use a composition comprising additionally a basic blast furnace slag, with the following ratio of the components (mass %):

soluble glass: 3-5

silicate component with the content of silicon dioxide exceeding 60 mass %: 15-50

limestone: 20-60

basic blast furnace slag: 10-30

aqueous acid solution with pH 1-2: 5-52

DESCRIPTION OF THE PREFERRED EMBODIMENTS

The preparation of the composition, according to the invention, is effected as follows. A mixture is prepared from dry ground components with the fineness of grinding up to 2000 cm² /g, using for this purpose, depending on the formulation, soluble glass in the form of silicate lump, limestone, a silicate component with the content of silicon dioxide exceeding 60 mass %, and basic blast furnace slag.

Quantitative selection of the components is defined by the prescribed physico-mechanical characteristics of the resulting composition and of the artificial stone material prepared therefrom. The prepared mixture is combined and stirred with the aqueous acid solution having pH of 1-4.

The soluble glass employed in the form of silicate lump differs from liquid glass in that it is a stock material for producing the latter.

As ground limestone, use is made of wastes resulting in sawing of building limestones, whose fraction is less than 0.14 mm, comprising (mass %): 49.23-52.3 CaO, 87.6-94 CaCO₃, 0.25-1.07 MgO, 0.52-2.23 MgCO₃, 2.86-8.1 SiO₂, 0.26-2.06 Fe₂ O₃, 0.2-1.12 Al₂ O₃, 0.05-0.16 SO₃, 0.04-0.59 K₂ O+Na₂ O.

Silicate components comprising more than 60 mass % of silicon dioxide can be either wastes of glass-making or tripoli clays with the specific surface of particles less than 2000 cm² /g.

Wastes of glass-making comprise (mass parts): 73.2-60.3 SiO₂ ; Al₂ O₃ +Fe₂ O₃ 12.0+1.2 CaO+MgO 12.3+9.0; Na₂ O+K₂ O 13.1+15.7 SO₃ 0.3-0.5 Mn₃ O₄ 0.5-1.5; Cr₂ O₃ 0.05-0.13.

An aqueous acid solution with pH 1-3 is a solution of boric, nitric, sulphuric, acetic acids or waste water of different acid-producing processes.

Basic blast furnace slag has a composition (mass parts): 41.24-35.71 SiO₂ ; 2.72-11.5 Al₂ O₃ ; 0.4-2.8 Fe₂ O₃ ; 34.9-47.13 CaO; 11.25-2.8 MgO; 0.66-2.6 SO₃ ; 0.36-5.2 MnO; up to 0.7 TiO₂.

The composition thus prepared, depending on the method employed, is shaped, compacted, and subjected to drying at the temperature of 250° C. during 4-8 hours. The resulting material is tested for ultimate compressive strength and ultimate bending strength at the temperature of 1000° C., its average density, heat conductivity, water resistance coefficient, and frost resistance are determined by following conventional procedures.

The essence of producing artificial stone materials, according to the invention, resides in the formation of silicic acid in the form of a winding film component when soluble glass is subjected to the effect of an aqueous acid solution with pH 1-4 during heat treatment. In this case a boundary interaction of this film with carbonate rock and formation of carbonate-silicate compounds occur, the latter strengthening the spatial skeleton of the resultant conglomerate. The mechanism of interaction of the acid introduced into the composition with other components is as follows. Upon introduction of the acid solution into the composition, dissolution of sodium silicate alongside of its hydrolysis with the formation of a silicic acid sol occurs. In the course of time and with temperature changes coagulation of the sol takes place and a gel possessing binding properties is formed. Since the course of hydrolysis proceeding with a sufficient speed depends only on the concentration of H⁺, the nature of the acid is not essential for the characteristics of the shaped stone material, these characteristics being determined only by the pH values of the acid solution introduced. The use of aqueous solutions of acids with pH 1-4 is dictated by two factors. If pH is lower than 1, in said composition gel formation occurs directly on the surface of sodium silicate, and the process does not develop in the bulk; as a result, the strength of the produced artificial material diminishes sharply. Furthermore, dissolution of the limestone takes place, and this lowers the activating effect of H⁺ on sodium silicate. In the case of pH higher than 4 hydrolysis proceeds only slightly because of a low concentration of H⁺ ; as a result, the strength characteristics of the stone materials produced do not attain the required values. Since the concentration of H⁺, necessary for the process, is defined only in the system of pH 1-4, it is possible to use organic and inorganic acids, different in the degree of hydrolysis.

Specific examples illustrating the embodiment of the present invention are given hereinbelow.

EXAMPLE 1

Dry ground components are mixed: soluble glass in the form of silicate lump, limestone, having the specific surface of up to 2000 cm² /g. Dry mixture is combined and stirred with an aqueous solution of boric acid with pH 1-4. From compositions whose formulations differ in the content of said components 4×4×15 cm samples are shaped by placing them into moulds, this being followed by vibration and heat treatment at the temperature of 250° C. for 5 hours. From the composition of formulation 5, presented hereinbelow in Table 1, samples are prepared by pressing at the pressure of 10 MPa and subsequent drying at the temperature of 250° C. for 5 hours. The samples are cooled, and then their average density, ultimate compressive strength, ultimate bending strength, water resistance coefficient, and frost resistance are determined.

The formulations of the prepared compositions and the physico-mechanical properties of artificial stone materials produced therefrom are listed in Table 1.

                                      TABLE 1                                      __________________________________________________________________________            Content of components, mass %                                                  Soluble    Aqueous    Ultimate                                          Composition                                                                           glass      solution of                                                                          Average                                                                             strength,   Frost Water                           formulation                                                                           (silicate  boric acid                                                                           density,                                                                            MPa         resistance,                                                                          resistance                      No.    lump)                                                                               Limestone                                                                            (pH)  kg/m.sup.3                                                                          compressive                                                                           bending                                                                             cycles                                                                               coefficient                     __________________________________________________________________________     1      65   20    15(2) 240  0.70   0.83 58    0.92                            2      55   10    35(3) 144  0.86   1.07 18    0.94                            3      45   20    35(3) 220  0.60   0.75 27    0.93                            4      47    1    52(4) 131  0.30   0.42 21    0.90                            5      20   75     5(1) 2100 76.0   26.0 410   0.92                            6       1   74    25(2) 1800 50.0   17.0 289   0.88                            __________________________________________________________________________

It is expedient to use formulations 1-4 for producing heat-insulating materials and formulations 5-6 for producing building materials having an enhanced frost resistance.

EXAMPLE 2

Dry ground components with the specific surface of 2000 cm² /g are mixed: silicate lump, limestone, and solicate component with the content of silicon dioxide exceeding 60 mass %. Dry mixture is combined and stirred with an aqueous solution of an acid with pH 1-4. The resulting compositions whose formulations differ in the content of said components in them are distributed into moulds and subjected to heat treatment at the temperature of 250° C. for 5 hours. The material thus produced is subjected to physico-mechanical tests.

The formulations of the compositions and the physicomechanical properties of the artificial stone materials made therefrom are listed in Table 2.

                                      TABLE 2                                      __________________________________________________________________________            Content of components, mass %                                                             Silicate                                                                  Soluble                                                                             component,                                                                           Aqueous   Ultimate                                                  glass                                                                               over 60                                                                              solution                                                                            Average                                                                             strength,            Heat                    Formulation  (silicate                                                                           mass %                                                                               of acid                                                                             density,                                                                            MPa         Water resistance                                                                        conductivity,           No.    Limestone                                                                            lump)                                                                               SiO.sub.2                                                                            (pH) kg/cm.sup.3                                                                         compressive                                                                           bending                                                                             coefficient                                                                             W/m · K        1      2     3    4     5    6    7      8    9        10                      __________________________________________________________________________     1       2    20   cullet                                                                               sulphuric                                                                            600 5.2    2.4  0.94     0.13                                      40    acid                                                                           38(4)                                                  2      10    40   20    30(3)                                                                                600 4.8    2.8  0.93     0.12                    3       6    30   30    34(4)                                                                                400 5.2    3.0  0.94     0.09                                      tripoli                                                                              nitric                                                                   clay  acid                                                   4       6    30   30    34(4)                                                                                350 5.3    2.2  0.94     0.07                    5       8    35   25    32(3)                                                                                500 5.0    3.1  0.94     0.10                    6       1     9   cullet                                                                               20(2)                                                                               2000 18.9   9.5  0.90     0.61                                      70                                                           7      64    15    1    20(2)                                                                               1800 18.8   10.9 0.90     0.58                    8      70     9    1    20(3)                                                                               2000 16.3   10.7 0.78     0.58                    9      30    11   40    19(1)                                                                               1900 35.2   16.7 0.90     0.58                                      tripoli                                                                              acetic                                                                   clay  acid                                                   10     30    10   40    20(2)                                                                               1900 34     16.8 0.88     0.55                    __________________________________________________________________________

The compositions with formulations 1-5 are recommendable to use for preparing heat insulating stone materials, whereas those with formulations 6-10 are preferable for preparing structural stone materials.

EXAMPLE 3

Ground components with the specific surface of up to 2000 g/cm² are mixed: silicate lump, limestone, silicate component with silicon dioxide content more than 60 mass %, basic blast furnace slag. Dry mixture is combined and stirred with an aqueous solution of nitric acid with pH 1-2. The composition thus prepared is moulded under the pressure of 10 MPa into 25.0×12.5×6.5 cm samples. The samples are dried at the temperature of 120° C. for 6 hours and subjected to roasting in a muffle furnace at the temperature of 1000° C. for 2 hours. After cooling the stone material thus produced, its physicomechanical properties are determined.

The formulations of the compositions, comprising said components in different amounts, and the physicomechanical properties of the stone materials manufactured therefrom are listed in Table 3.

                                      TABLE 3                                      __________________________________________________________________________            Content of components, mass %                                                             Silicate                                                                  Soluble                                                                             component,                                                                           Basic                                                                              Aqueous                                            Composition  glass                                                                               over 60                                                                              blast                                                                              solution                                                                             Average                                                                             Ultimate strength, MPa                  formulation  (silicate                                                                           mass %                                                                               furnace                                                                            of HNO.sub.3                                                                         density,                                                                            compressive                             No.    Limestone                                                                            lump)                                                                               SiO.sub.2                                                                            slag                                                                               (pH)  kg/m.sup.3                                                                          at 1000° C.                                                                    compressive                                                                           bending                   1      2     3    4     5   6     7    8      9      10                        __________________________________________________________________________     1      20    3    cullet                                                                               17  10(1) 2310 2      10.7   3.1                                         50                                                           2      30    5    25    30  10(2) 2200 1      29.8   10.0                      3      40    4    32    14  10(1) 2290 1      30.0   9.8                       4      45    5    30    10  10(2) 2300 1      25.2   10.2                      5      60    5    tripoli                                                                              10  10(1) 2430 1      10.1   3.2                                         clay                                                                           15                                                           __________________________________________________________________________

Materials made from the herein-proposed composition will find extensive application in the manufacture of building and technological structures, heat insulating coatings, heat-resistant elements and facing plates. 

What is claimed is:
 1. A composition for preparing artificial stone materials, consisting of a silicate component, limestone, and an aqueous solution of an acid with pH 1-4, said silicate component consisting of soluble glass, said composition having the following ratio of the components (mass %):soluble glass: 3-65 limestone: 1-75 aqueous solution of an acid with pH 1-4: 5-52.
 2. A composition according to claim 1, further consisting of a silicate component with the content of silicon dioxide exceeding 60 mass %, with the following ratio of the components (mass %);soluble glass: 3-40 silicate component with the content of silicon dioxide exceeding 60 mass %: 1-70 limestone: 1-70 aqueous solution of an acid with pH 1-4: 5-52.
 3. A composition according to claim 2, consisting of components with the following ratio thereof (mass %):soluble glass: 9-15 silicate component with the content of silicon dioxide exceeding 60 mass %: 1-70 limestone: 1-70 aqueous solution of an acid with pH 2-4: 5-52.
 4. A composition according to claim 2, consisting of components with the following ratio thereof (mass %):soluble glass: 20-40 silicate component with the content of silicon dioxide exceeding 60 mass %: 20-40 limestone: 2-10 aqueous solution of an acid with pH 1-3: 5-52.
 5. A composition according to claim 2, wherein said silicate component consists of wastes of glass-making process or tripoli clays.
 6. A composition according to claim 2, further consisting of basic blast furnace slag, with the following ratio of the components (mass %):soluble glass: 3-5 silicate component with the content of silicon dioxide exceeding 60 mass %: 15-50 limestone: 20-60 basic blast furnace slag: 10-30 aqueous solution of an acid with pH 1-2: 5-52.
 7. A composition according to claim 1, wherein said aqueous solution of an acid with pH 1-4 consists of waste water of acid-manufacturing processes. 